护坡钢模具是护坡模具中钢材质的一种，那么对于护坡钢模具的制作工艺大家又了解多少呢!护坡钢模具工艺具有以下几点：
The slope protection steel mold is one of the steel materials in the slope protection mold, so how much do you know about the production process of the slope protection steel mold? The slope protection steel mold process has the following points:
1、可锻性：具有较低的热锻变形抗力，塑性好，锻造温度范围宽，锻裂冷裂及析出网状碳化物倾向低。
1. Malleability: it has low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency of forging crack, cold crack and precipitation network carbide.
2、退火工艺性：球化退火温度范围守则，退火硬度低且波动范围小，球化率高。
2. Annealing process: spheroidizing annealing temperature range rules, low annealing hardness and fluctuation range, high spheroidizing rate.
3、切削加工性：切削用量大，刀具损耗低，加工表面粗糙度低。3. Machinability: large cutting parameters, low tool loss and low surface roughness.
4、氧化、脱碳敏感性：高温加热时抗氧化功能好，脱碳速度慢，对加热介质不敏感，产生麻点倾向小。
4. Oxidation and decarburization sensitivity: when heated at high temperature, the oxidation resistance is good, the decarburization rate is slow, and it is not sensitive to the heating medium, and the pitting tendency is small.
5、淬硬性：淬火后具有均匀而高的表面硬度。5. Hardenability: uniform and high surface hardness after quenching.
6、淬透性：淬火后能获得较深的淬硬层，采用缓和的淬火介质就能淬硬。6. Hardenability: a deeper hardened layer can be obtained after quenching, which can be hardened by using mild quenching medium.
7、淬火变形开裂倾向常规淬火体积变化小，形状翘曲，畸变轻微，异常变形倾向低。常规淬火开裂敏感性低，对淬火温度及工件形状不敏感。
7. Quenching deformation cracking tendency conventional quenching volume change is small, shape warpage, distortion is slight, abnormal deformation tendency is low. The cracking sensitivity of conventional quenching is low, and it is not sensitive to quenching temperature and workpiece shape.
8.可磨削性：砂轮相对损耗小，无烧伤极限磨削用量大，对砂轮质量及冷却条件不敏感，不易发生磨伤及磨削裂纹。
8. Grindability: the grinding wheel has small relative loss, no burn limit, large grinding consumption, insensitive to the grinding wheel quality and cooling conditions, and is not easy to cause grinding damage and grinding cracks.
以上就是对护坡钢模具的制作工艺详细介绍！The above is a detailed introduction to the production process of slope protection steel!